2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
58.8 (8530) - 0.8 mil (20 µm)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
63.0 (9140) - 2.0 mil (51 µm)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
>850 g - 0.8 mil (20 µm)
|
Density
|
0.904 g/cm3
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
960 g - 2.0 mil (51 µm)
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
1100 g - 2.0 mil (51 µm)
|
Fabrication Method
|
Sheet Extrusion
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
Gloss (45 degree)
|
90 - 2.00 mil (50.8 µm)
|
Haze (ASTM D1003)
|
1.80 - 2.00 mil (50.8 µm) %
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
4
|
Melting Point, DSC (Dow Method) in °C(°F)
|
124 (255)
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
17.5 (211) - 2.0 mil (51 µm)
|
Tensile Elongation at Break, MD
|
660 - 2.0 mil (51 µm) %
|
Tensile Elongation at Break, TD
|
710 - 2.0 mil (51 µm) %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
32.6 (4730) - 2.0 mil (51 µm)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
32.4 (4700) - 2.0 mil (51 µm)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
6.76 (980) - 2.0 mil (51 µm)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
6.34 (919) - 2.0 mil (51 µm)
|
Vicat Softening Point in °C(°F)
|
71.1 (160)
|