2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
219 (31700)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
248 (36000)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
> 850 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
720 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
1000 g
|
|
Enhanced LLDPE
|
Yes
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
58
|
|
Haze (ASTM D1003)
|
15 %
|
|
Heat Seal Initiation Temp in °C(°F)
|
106 (223)
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
121 (250)
|
|
Vicat Softening Point in °C(°F)
|
105 (221)
|