2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
798 (116000)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
887 (129000)
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance
|
Impact Strength in MPa (psi)
|
76 J/m (1.4 ft-lb/in) - Notched Izod Impact (23˚C (73˚F))
|
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238))
|
11
|
Melt Index (g/10min @190°C/5.0 kg (ASTM D1238))
|
0.38
|
Tensile Elongation at Break, MD
|
310 %
|
Tensile Elongation at Break, TD
|
610 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
34.8 (5050)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
26.0 (3770)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
16.0 (2330)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
18.0 (2610)
|