2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1050 (152000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1050 (152000)
|
|
Density Range
|
.961+
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
77 kJ/m2 (36.6 ft lb/in2) ASTM D1822
|
|
Structure Type
|
Monolayer
|
|
Tensile Elongation at Break, MD
|
800 %
|
|
Tensile Elongation at Break, TD
|
800 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
32 (4640)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
32 (4640)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
29 (4210)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
29 (4210)
|