Propiedades

Propiedades clave

Density 0.95 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 33
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 33

Beneficios de la Aplicación

Anti-block No
Slip No

Propiedades tipicas

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 1000 (145000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 1000 (145000)
Density Range .940-.950
Fabrication Method Injection Molding
Functionality Mechanical Performance
Structure Type Monolayer, Multilayer
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 13.8 (2000)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 13.8 (2000)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 26.9 (3900)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 26.9 (3900)