2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
669 (97000) ASTM D638
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
669 (97000) ASTM D638
|
|
Density Range
|
.951-.960
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Structure Type
|
Monolayer, Multilayer
|
|
Tensile Elongation at Break, MD
|
700 %
|
|
Tensile Elongation at Break, TD
|
700 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
16.5 (2400)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
16.5 (2400)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
20.7 (3000)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
20.7 (3000)
|