Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
180 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
190 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
390 g
|
Fabrication Method
|
Sheet Extrusion
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
4
|
Melting Point, DSC (Dow Method) in °C(°F)
|
190 to 260 (374 to 500)
|
Tensile Elongation at Break, MD
|
500 - 0.91 mil (23 µm) %
|
Tensile Elongation at Break, TD
|
630 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
33.0 (4790)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
23.0 (3340)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
4.30 (624)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
3.60 (522)
|
Vicat Softening Point in °C(°F)
|
72 (162)
|