Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
120 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
280 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
570 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Processing
|
|
Gloss (45 degree)
|
91
|
|
Haze (ASTM D1003)
|
4.8 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
113 (235)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
5.46 J/cm3 (66 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
440 %
|
|
Tensile Elongation at Break, TD
|
600 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
30.2 (4380)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
25.4 (3680)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
15.4 (2240)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
14.2 (2050)
|