2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
200 (29000)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
228 (33000)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
170 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
220 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
210 g
|
Fabrication Method
|
Blown Film Extrusion, Blown Film Extrusion
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
0.22
|
Melting Point, DSC (Dow Method) in °C(°F)
|
109 (228)
|
Tensile Elongation at Break, MD
|
220 %
|
Tensile Elongation at Break, TD
|
500 %
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
11 (1600)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11 (1600)
|