2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
221 (32100)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
255 (37000)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
75 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
290 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
95 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Sealant (non-peelable)
|
Melting Point, DSC (Dow Method) in °C(°F)
|
109 (228)
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
2.48 J/cm3 (30 ft lb/in3)
|
Tensile Elongation at Break, MD
|
110 %
|
Tensile Elongation at Break, TD
|
430 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
29.6 (4300)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
16.2 (2350)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
28.3 (4100)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
13 (1880)
|
Vicat Softening Point in °C(°F)
|
94 (201)
|