2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
216 (31400)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
256 (37200)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
70 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
270 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
95 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Sealant (non-peelable)
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
0.65
|
Melting Point, DSC (Dow Method) in °C(°F)
|
109 (228)
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4.96 J/cm3 (60 ft lb/in3)
|
Tensile Elongation at Break, MD
|
120 %
|
Tensile Elongation at Break, TD
|
440 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
28.6 (4150)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
16.9 (2450)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
27.6 (4000)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
12.8 (1850)
|
Vicat Softening Point in °C(°F)
|
94 (201)
|