Propiedades

app.properties.Title

Anti-block No
Slip false

typical.properties.Title

Density 0.8995 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 78 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 410 g
Fabrication Method Blown Film Extrusion, Cast Film Extrusion, Extrusion Coating and Lamination
Functionality Sealant (non-peelable)
Haze (ASTM D1003) 4 %
Heat Seal Initiation Temp in °C(°F) 88 (190)
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238)) 6
Melting Point, DSC (Dow Method) in °C(°F) 96 (205)
Tensile Elongation at Break, MD 470 %
Tensile Elongation at Break, TD 720 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 48 (6960)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 30 (4350)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 5.8 (841)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 5.3 (769)
Vicat Softening Point in °C(°F) 81 (178)