Density
|
0.902 g/cm3
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
550 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
720 g
|
|
Fabrication Method
|
Blown Film Extrusion, Foam Extrusion, Sheet Extrusion
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
1.1 %
|
|
Heat Seal Initiation Temp in °C(°F)
|
85 (185)
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
1, 1
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
99 (210)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
22.3 (270 )
|
|
Structure Type
|
Multilayer
|
|
Tensile Elongation at Break, MD
|
620 %
|
|
Tensile Elongation at Break, TD
|
630 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
58.6 (8500)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
44.7 (6480)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
7.24 (1050)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
6.89 (1000)
|
|
Vicat Softening Point in °C(°F)
|
86 (187)
|