Density
|
0.876 g/cm3
|
|
Fabrication Method
|
Blow Molding, Blown Film Extrusion, Oriented (Biaxially), Oriented (Machine Direction), Sheet Extrusion
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
3.9 %
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
8
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
85 (185)
|
|
Tensile Elongation at Break, MD
|
840 (ASTM D638) %
|
|
Tensile Elongation at Break, TD
|
840 (ASTM D638) %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
22.1 (3210) (ASTM D638)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
22.1 (3210) (ASTM D638)
|
|
Vicat Softening Point in °C(°F)
|
59 (138)
|