性能
key.properties.Title |
|
|---|---|
| Density | 0.902 g/cm3 |
| Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) | 0.85 (g/10min @190°C/2.16 kg) (ASTM D1238) |
typical.properties.Title |
|
|---|---|
| Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) | 640 g |
| Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) | 320 g |
| Fabrication Method | Blown Film Extrusion |
| Gloss (45 degree) | 79 |
| Haze (ASTM D1003) | 3 % |
| Tensile Elongation at Break, MD | 480 % |
| Tensile Elongation at Break, TD | 530 % |
| Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 23.1 (3350) |
| Tensile Strength Break, TD (ASTM D882) in MPa (psi) | 18.7 (2710) |
| Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 3.50 (508) |
| Tensile Strength Yield, TD (ASTM D882) in MPa (psi) | 4.80 (696) |