性能

关键属性

Density 0.908 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.85

应用优势

Anti-block Yes
Slip Yes

典型特性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 68.9 (10000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 77.2 (11200)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 1000 g
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 210 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 430 g
Enhanced LLDPE Yes
Fabrication Method Blown Film Extrusion
Functionality Mechanical Performance, Sealant (non-peelable)
Gloss (45 degree) 63
Haze (ASTM D1003) 7.9 %
Melting Point, DSC (Dow Method) in °C(°F) 106 (223)
Tensile Elongation at Break, MD 450 %
Tensile Elongation at Break, TD 600 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 49 (7100)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 40 (5800)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 7.93 (1150)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 7.79 (1130)