2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
159 (23000)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
165 (24000)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
450 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
250 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
550 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
1
|
Melting Point, DSC (Dow Method) in °C(°F)
|
123 (253)
|
Vicat Softening Point in °C(°F)
|
100 (212)
|