性能
关键属性 |
|
|---|---|
| Density | 0.934 g/cm3 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 1.7 |
应用优势 |
|
|---|---|
| Anti-block | No |
| Slip | No |
典型特性 |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 420 (ISO 527-3) |
| 2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 470 (ISO 527-3) |
| Dart Drop Impact (ASTM D1709A) in grams (lbs) | 110 g (ISO 527-3) |
| Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) | 130 g |
| Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) | 230 g |
| Enhanced LLDPE | No |
| Fabrication Method | Blown Film Extrusion |
| Functionality | Mechanical Performance |
| Vicat Softening Point in °C(°F) | 124 (255) |