性能
关键属性 |
|
|---|---|
| Density | 0.919 g/cm3 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 0.80 |
应用优势 |
|
|---|---|
| Anti-block | Yes |
| Slip | Yes |
典型特性 |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 182 (26400) |
| 2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 192 (27800) |
| Dart Drop Impact (ASTM D1709A) in grams (lbs) | 560 g |
| Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) | 410 g |
| Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) | 640 g |
| Enhanced LLDPE | No |
| Fabrication Method | Blown Film Extrusion |
| Functionality | Mechanical Performance |
| Gloss (45 degree) | 62 |
| Haze (ASTM D1003) | 9.1 % |
| Melting Point, DSC (Dow Method) in °C(°F) | 118 (244) |