性能
关键属性 |
|
|---|---|
| Density | 0.941 g/cm3 |
| Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) | 0.55 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 0.55 |
应用优势 |
|
|---|---|
| Anti-block | No |
| Slip | No |
典型特性 |
|
|---|---|
| Fabrication Method | Compression Molding, Pipe Extrusion |
| Tensile Elongation at Break, MD | 780 % |
| Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 37.0 (5370) |
| Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 20.3 (2940) |
| Vicat Softening Point in °C(°F) | 125 (256) |