性能

app.properties.Title

Anti-block No
Slip No
Tie Layers No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 2.0 mil - 194 (28200)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 2.0 mil - 233 (33700)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 290 g - 2.0 mil
Density 0.92 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 2.0 mil - 900
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 2.0 mil - 1200
Enhanced LLDPE No
Fabrication Method Blown Film Extrusion, Cast Film Extrusion
Functionality Mechanical Performance
Gloss (45 degree) 63
Haze (ASTM D1003) 9 %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 1
Melting Point, DSC (Dow Method) in °C(°F) 122 (252)
Vicat Softening Point in °C(°F) 108 (226)