性能

关键属性

Density 0.918 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 2.3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 2.3

应用优势

Anti-block No
Closure Type Caps, Pull Tabs
Slip No

产品使用和配方

Type Breathable Cast Film, Non-Breathable Cast Film

典型特性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 166 (24100)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 208 (30200)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 96 g
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 320 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 190 g
Fabrication Method Blown Film Extrusion
Functionality Optical Performance, Processing
Gloss (45 degree) 40
Haze (ASTM D1003) 16.1 %
Melting Point, DSC (Dow Method) in °C(°F) 108 (226)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 3.56 J/cm3 (43 ft lb/in3)
Tensile Elongation at Break, MD 450 %
Tensile Elongation at Break, TD 620 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 21.8 (3160)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 19.6 (2850)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 11.6 (1690)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11 (1600)
Vicat Softening Point in °C(°F) 92.2 (198)