2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
175 (25600)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
185 (26800)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
170 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
350 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
260 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Optical Performance, Processing
|
|
Gloss (45 degree)
|
58
|
|
Haze (ASTM D1003)
|
9.2 %
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4 J/cm3 (48.3 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
390 %
|
|
Tensile Elongation at Break, TD
|
570 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
25 (3630)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
23 (3340)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
11 (1600)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11 (1600)
|