Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
100 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
430 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
390 g
|
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion
|
|
Functionality
|
Optical Performance, Processing
|
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
3
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
2 J/cm3 (24.2 ft lb/in3)
|
|
Structure Type
|
Monolayer, Multilayer
|
|
Tensile Elongation at Break, MD
|
550 %
|
|
Tensile Elongation at Break, TD
|
750 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
50 (2900)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
15 (2180)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
11 (1600)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11 (1600)
|