Density 0.921 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 2

应用优势

Anti-block Yes
Slip Yes

典型特性

Dart Drop Impact (ASTM D1709A) in grams (lbs) 120 g
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 430 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 310 g
Fabrication Method Blown Film Extrusion, Cast Film Extrusion
Functionality Optical Performance, Processing
Gloss (45 degree) 58
Haze (ASTM D1003) 10 %
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 3 J/cm3 (36.3 ft lb/in3)
Tensile Elongation at Break, MD 520 %
Tensile Elongation at Break, TD 800 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 19 (2760)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 19 (2760)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 10 (1450)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11 (1600)