2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
128 (18600)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
128 (18600)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
430 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
270 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
480 g
|
Fabrication Method
|
Blown Film Extrusion, Blown Film Extrusion
|
Functionality
|
Optical Performance, Processing
|
Tensile Elongation at Break, MD
|
470 %
|
Tensile Elongation at Break, TD
|
530 %
|
Vicat Softening Point in °C(°F)
|
96 (205)
|