性能

关键属性
Density 0.952 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 10

应用优势
Anti-block No
Closure Type Caps, Hot Fill / Aseptic, Still Water
Slip No

典型特性
2% Secant Modulus, MD (ASTM D882) in MPa (psi) 1050 (152000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 1050 (152000)
Density Range .951-.960
ESCR-Environmental Stress Crack Resistance (10% IGEPAL) 12 hr
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 22 hr
Fabrication Method Compression Molding, Injection Molding
Functionality Mechanical Performance
Tensile Elongation at Break, MD 1500 %
Tensile Elongation at Break, TD 1500 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 20.5 (2970)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 20.5 (2970)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 27.3 (3960)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 27.3 (3960)