性能

关键属性

Density 0.961 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 57
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.8, 0.80

应用优势

Anti-block No
Slip No

典型特性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 1300 (188000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 1300 (188000)
Brittleness Temperature in °C(°F) < -76.1
Density Range .961+
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 20 hr
Fabrication Method Sheet Extrusion
Functionality Mechanical Performance
Impact Strength in MPa (psi) 84 kJ/m2 (40 ft lb/in2) ASTM D1822
Tensile Elongation at Break, MD 1000 %
Tensile Elongation at Break, TD 1000 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 24 (3480)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 24 (3480)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 32 (4640)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 32 (4640)