性能

app.properties.Title

Anti-block No
Closure Type Fitments, Hinges, Pull Tabs
Slip Yes

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 317 (46000) (ASTM D790)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 317 (46000) (ASTM D790)
Density 0.923 g/cm3
Fabrication Method Injection Molding
Functionality Mechanical Performance
Impact Strength in MPa (psi) 252 kJ/m2 (120 ft lb/in2) ASTM D1822
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 25
Melting Point, DSC (Dow Method) in °C(°F) 110 (230)
Tensile Elongation at Break, MD 40 (ASTM D638) %
Tensile Elongation at Break, TD 40 (ASTM D638) %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 11.7 (1700) (ASTM D638)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 10.3 (1500) (ASTM D638)