性能

app.properties.Title

Anti-block Yes
Collation Shrink Usage Retail
Slip Yes

typical.properties.Title

Dart Drop Impact (ASTM D1709A) in grams (lbs) Blown Film - 87 g
Density 0.923 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) Blown Film - 450 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) Blown Film - 430 g
Fabrication Method Blown Film Extrusion, Cast Film Extrusion
Functionality Optical Performance, Processing
Gloss (45 degree) 87
Haze (ASTM D1003) Blown Film - 5.7 %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 2.6
Melting Point, DSC (Dow Method) in °C(°F) 113 (235)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) Blown Film - 3.47 J/cm3 (42 ft lb/in3)
Tensile Elongation at Break, MD Blown Film - 780 %
Tensile Elongation at Break, TD Blown Film - 580 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) Blown Film - 23.4 (3400)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) Blown Film - 20.6 (2990)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) Blown film - 12.5 (1810)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) Blown Film - 12.7 (1840)
Vicat Softening Point in °C(°F) 97.2 (207)