性能

关键属性

Density 0.924 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 4.2

应用优势

Anti-block No
Slip No

典型特性

Dart Drop Impact (ASTM D1709A) in grams (lbs) 27 g
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 310 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 80 g
Fabrication Method Cast Film Extrusion, Extrusion Coating and Lamination
Functionality Mechanical Performance
Gloss (45 degree) 51
Haze (ASTM D1003) 12.9 %
Melting Point, DSC (Dow Method) in °C(°F) 112 (234)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 2.32 J/cm3 (28 ft lb/in3)
Tensile Elongation at Break, MD 220 %
Tensile Elongation at Break, TD 610 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 31 (4500)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 17 (2470)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 14.8 (2140)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 10.9 (1580)
Vicat Softening Point in °C(°F) 95 (203)