性能

关键属性

Density 0.953 g/cm3
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 10

应用优势

Anti-block No
Slip No

典型特性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 870 (126000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 870 (126000)
Density Range .951-.960
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) >1000 hr
Fabrication Method Blow Molding
Functionality Mechanical Performance
Melt Index (g/10min @190°C/5.0 kg (ASTM D1238)) 0.41
Tensile Elongation at Break, MD 900 %
Tensile Elongation at Break, TD 900 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 40 (5800)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 40 (5800)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 25 (3630)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 25 (3630)