性能

关键属性

Density 0.954 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 7

应用优势

Anti-block No
Slip No

典型特性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 669 (97000) ASTM D638
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 669 (97000) ASTM D638
Density Range .951-.960
Fabrication Method Injection Molding
Functionality Mechanical Performance
Structure Type Monolayer, Multilayer
Tensile Elongation at Break, MD 700 %
Tensile Elongation at Break, TD 700 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 16.5 (2400)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 16.5 (2400)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 20.7 (3000)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 20.7 (3000)