性能

关键属性

Density 0.958 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 5

应用优势

Anti-block No
Slip No

产品使用和配方

Type Breathable Cast Film, Non-Breathable Cast Film

典型特性

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 472 (68500) ASTM D882
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 672 (97500) ASTM D882
Density Range .951-.960
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 44 hr
Fabrication Method Cast Film Extrusion, Injection Molding
Functionality Mechanical Performance
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 3.31 (40)
Structure Type Monolayer, Multilayer
Tensile Elongation at Break, MD 600 %
Tensile Elongation at Break, TD 650 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 36 (5220) ASTM D882
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 28 (4060) ASTM D882
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 27 (3920) ASTM D882
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 28 (4060) ASTM D882