DOW™ LDPE 410E Low Density Polyethylene Resin

A high clarity resin designed for lamination film and clarity over wrap applications. This resin does not contain slip and antiblock additives. It can be readily extruded using conventional blown film techniques utilising melt temperatures between 170 and 195°C and cast film using temperatures between 180 and 240 °C. This resin when properly fabricated shows: excellent processability and draw down, outstanding toughness and impact properties, superior optical properties, excellent tensile and tear strength. Applications: - Lamination films - Food packaging films - Hygiene films - Cast films - Air-bubble film - Foamed PE - Extrusion coating



  • 2% Secant Modulus, MD (ASTM D882) in MPa (psi) 190 (27600)
  • 2% Secant Modulus, TD (ASTM D882) in MPa (psi) 200 (29000)
  • Dart Drop Impact (ASTM D1709A) in grams (lbs) 110 g
  • Density (ASTM D792) 0.925 g/cm3
  • Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 500 g
  • Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 400 g
  • Gloss (45 degree) 80 %
  • Haze (ASTM D1003) 6.9 %
  • Melt Index (g/10min @190°C/21.6 kg) 2
  • Tensile Elongation at Break, MD 450 %
  • Tensile Elongation at Break, TD 650 %
  • Tensile Strength Break, MD (ASTM D882) in MPa (psi) 22 (3190)
  • Tensile Strength Break, TD (ASTM D882) in MPa (psi) 20 (2900)
  • Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 10 (1450)
  • Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11 (1600)
  • Vicat Softening Point in °C(°F) 96 (205)