Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
700 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
900 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
1400 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance, Optical Performance
|
Tensile Elongation at Break, MD
|
580 %
|
Tensile Elongation at Break, TD
|
720 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
23 (3340)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
24 (3480)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10 (1450)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
11 (1600)
|