Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
180 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
200 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
360 g
|
|
Fabrication Method
|
Sheet Extrusion
|
|
Flow Index (g/10 min)
|
3.3
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Gloss (45 degree)
|
92
|
|
Haze (ASTM D1003)
|
0.7 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
190 to 260 (374 to 500)
|
|
Tensile Elongation at Break, MD
|
450 - 0.91 mil (23 µm) %
|
|
Tensile Elongation at Break, TD
|
600 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
28.0 (4060)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
25.0 (3630)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
4.80 (696)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
4.50 (653)
|
|
Vicat Softening Point in °C(°F)
|
90 (194)
|