2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
89.6 (13000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
93.8 (13600)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
>1100 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
370 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
520 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Flow Index (g/10 min)
|
0.80
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Gloss (45 degree)
|
39
|
|
Haze (ASTM D1003)
|
14 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
123 (253)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
24.8 (300)
|
|
Tensile Elongation at Break, MD
|
340 %
|
|
Tensile Elongation at Break, TD
|
570 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
32.4 (4700)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
30.0 (4350)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
6.21 (900)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
5.86 (850)
|
|
Vicat Softening Point in °C(°F)
|
83.9 (183)
|