Density
|
0.904 g/cm3
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
560 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
730 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance, Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
3.2 %
|
|
Heat Seal Initiation Temp in °C(°F)
|
85 (185)
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
1
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
100 (212)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
21.9 (265 )
|
|
Tensile Elongation at Break, MD
|
590 %
|
|
Tensile Elongation at Break, TD
|
630 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
45.4 (6580)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
42.5 (6170)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
8.07 (1170)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
7.17 (1040)
|
|
Vicat Softening Point in °C(°F)
|
86 (187)
|