Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
11g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
25g
|
|
Fabrication Method
|
Sheet Extrusion
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
3.6
|
|
Tensile Elongation at Break, MD
|
1100 %
|
|
Tensile Elongation at Break, TD
|
1400 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
7.86 (1140)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
4.31 (625)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
1.63 (236)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
1.20 (174)
|