Density
|
0.900 g/cm3
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
78 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
410 g
|
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion, Extrusion Coating and Lamination
|
|
Functionality
|
Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
4 %
|
|
Heat Seal Initiation Temp in °C(°F)
|
88 (190)
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
6
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
96 (205)
|
|
Tensile Elongation at Break, MD
|
470 %
|
|
Tensile Elongation at Break, TD
|
720 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
48 (6960)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
30 (4350)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
5.8 (841)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
5.3 (769)
|
|
Vicat Softening Point in °C(°F)
|
81 (178)
|