2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
181 (26200)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
207 (30000)
|
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
150 g
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
500 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
280 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Mechanical Performance
|
|
Gloss (45 degree)
|
66
|
|
Haze (ASTM D1003)
|
7.6 %
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
112 (233)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
2.9 J/cm3 (35 ft lb/in3)
|
|
Tensile Elongation at Break, MD
|
420 %
|
|
Tensile Elongation at Break, TD
|
670 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
24.8 (2600)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
23 (3330)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
12.3 (1790)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
12.1 (1760)
|
|
Vicat Softening Point in °C(°F)
|
98.3 (209)
|