Density
|
0.909 g/cm3
|
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
560 g
|
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
840 g
|
|
Fabrication Method
|
Blown Film Extrusion
|
|
Functionality
|
Sealant (non-peelable)
|
|
Haze (ASTM D1003)
|
2.5 %
|
|
Heat Seal Initiation Temp in °C(°F)
|
92.8 (199)
|
|
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238))
|
1
|
|
Melting Point, DSC (Dow Method) in °C(°F)
|
106 (222)
|
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
25.2 (304 )
|
|
Tensile Elongation at Break, MD
|
620 %
|
|
Tensile Elongation at Break, TD
|
580 %
|
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
47.8 (6930)
|
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
45.4 (6580)
|
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
8.76 (1270)
|
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
8.07 (1170)
|
|
Vicat Softening Point in °C(°F)
|
95 (203)
|