DOW™ LDPE 312E Low Density Polyethylene Resin

A fractional melt index low density polyethylene resin, containing slip and antiblock additives. This product has been specially designed for superior processability on blown film lines leading to significant output improvements. The resin offers additionally excellent draw down. It can be used pure or in blends with LLDPE resins. Applications: Health & hygiene films, Food packaging, Collation shrink, Agricultural films, Shopping bags, Garbage bags, Lamination films Main Characteristics: - Excellent processability and draw down - Good physical properties in blends with LLDPE - Can be readily extruded using conventional blown film techniques at melt temperatures between 160 and 195°C DOW LDPE 312E should compliy with: - U.S. FDA 21 CFR 177.1520 (c)2.2 - EU, No 10/2011 - Canadian HPFB No Objection - U.S. FDA-DMF - Consult the regulations for complete details.



  • 2% Secant Modulus, MD (ASTM D882) in MPa (psi) 175 (25400)
  • 2% Secant Modulus, TD (ASTM D882) in MPa (psi) 185 (26800)
  • Dart Drop Impact (ASTM D1709A) in grams (lbs) 170 g
  • Density (ASTM D792) 0.923 g/cm3
  • Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 350 g
  • Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 260 g
  • Gloss (45 degree) 58 %
  • Haze (ASTM D1003) 9.2 %
  • Melt Index (g/10min @190°C/21.6 kg) 0.75
  • Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 4 J/cm3 (48.3 ft lb/in3)
  • Tensile Elongation at Break, MD 380 %
  • Tensile Elongation at Break, TD 570 %
  • Tensile Strength Break, MD (ASTM D882) in MPa (psi) 25 (3630)
  • Tensile Strength Break, TD (ASTM D882) in MPa (psi) 23 (3340)
  • Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 11 (1600)
  • Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11 (1600)