[{"values":[{"value":"日本語-日本","languageCode":"ja-jp","link":"javascript:void(0);"},{"value":"中文","languageCode":"zh-cn","link":"javascript:void(0);"},{"value":"English-英语","languageCode":"en-us","link":"javascript:void(0);"}],"label":"JP","default":"ja-jp"},{"values":[{"value":"日本語-日本","languageCode":"ja-jp","link":"javascript:void(0);"},{"value":"中文","languageCode":"zh-cn","link":"javascript:void(0);"},{"value":"English-英语","languageCode":"en-us","link":"javascript:void(0);"}],"label":"CN","default":"zh-cn"},{"values":[{"value":"日本語-日本","languageCode":"ja-jp","link":"javascript:void(0);"},{"value":"中文","languageCode":"zh-cn","link":"javascript:void(0);"},{"value":"English-英语","languageCode":"en-us","link":"javascript:void(0);"}],"label":"US","default":"en-us"}]

DOW™ HDPE 40055L HF High Density Polyethylene Resin

Bimodal, high density polyethylene with good stress crack resistance, impact resistance, and stiffness that is used in a variety of applications such as agrochemical and agressive liquid containers​​

性能

这些数值为典型性能,并且不用于在规格制定过程中使用。

  • 2% Secant Modulus, MD (ASTM D882) in MPa (psi) 870 (126000)
  • 2% Secant Modulus, TD (ASTM D882) in MPa (psi) 870 (126000)
  • Anti-block false
  • Density (ASTM D792) 0.953 g/cm3
  • ESCR-Environmental Stress Crack Resistance (100% IGEPAL) > 1000 hr
  • Melt Index (g/10min @190°C/21.6 kg) 10 g/10minutes (190°C/21.6 kg), 0.42 g/10minutes (190°C/5.0 kg)
  • Slip false
  • Tensile Elongation at Break, MD 900 %
  • Tensile Elongation at Break, TD 900 %
  • Tensile Strength Break, MD (ASTM D638) in MPa (psi) 40 (5800)
  • Tensile Strength Break, TD (ASTM D638) in MPa (psi) 40 (5800)
  • Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 25 (3630)
  • Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 25 (3630)

此材料没有安全数据说明书
如需了解更多信息,请 联系陶氏

没有找到此材料按所选语言显示的销售规格

DOW™ HDPE 40055L HF High Density Polyethylene Resin
该产品暂无技术数据表
如需了解更多信息,请 联系陶氏

DOW™ HDPE 40055L HF High Density Polyethylene Resin


该产品暂无法规信息说明书


DOW™ HDPE 40055L HF High Density Polyethylene Resin
如需了解该产品的经销商选项,请 联系陶氏