[{"values":[{"value":"日本語-日本","languageCode":"ja-jp","link":"javascript:void(0);"},{"value":"中文","languageCode":"zh-cn","link":"javascript:void(0);"},{"value":"English-英语","languageCode":"en-us","link":"javascript:void(0);"}],"label":"JP","default":"ja-jp"},{"values":[{"value":"日本語-日本","languageCode":"ja-jp","link":"javascript:void(0);"},{"value":"中文","languageCode":"zh-cn","link":"javascript:void(0);"},{"value":"English-英语","languageCode":"en-us","link":"javascript:void(0);"}],"label":"CN","default":"zh-cn"},{"values":[{"value":"日本語-日本","languageCode":"ja-jp","link":"javascript:void(0);"},{"value":"中文","languageCode":"zh-cn","link":"javascript:void(0);"},{"value":"English-英语","languageCode":"en-us","link":"javascript:void(0);"}],"label":"US","default":"en-us"}]

DOW™ 955I Low Density Polyethylene Resin

Low Density Polyethylene (LDPE). Typical applications include lids, caps/closures, general purpose. It has excellent clarity.

性能

这些数值为典型性能,并且不用于在规格制定过程中使用。

  • 2% Secant Modulus, MD (ASTM D882) in MPa (psi) 296 (43000) (ASTM D790)
  • 2% Secant Modulus, TD (ASTM D882) in MPa (psi) 296 (43000) (ASTM D790)
  • Density (ASTM D792) 0.923 g/cm3
  • Impact Strength in MPa (psi) 252 kJ/m2 (120 ft lb/in2) ASTM D1822
  • Melt Index (g/10min @190°C/21.6 kg) 35
  • Melting Point, DSC (Dow Method) in °C(°F) 112°C (234°F)
  • Tensile Elongation at Break, MD 90 (ASTM D638) %
  • Tensile Elongation at Break, TD 90 (ASTM D638) %
  • Tensile Strength Break, MD (ASTM D882) in MPa (psi) 6.89 (1000) (ASTM D638)
  • Tensile Strength Break, TD (ASTM D882) in MPa (psi) 6.89 (1000) (ASTM D638)
  • Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 9.65 (1400) (ASTM D638)
  • Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 9.65 (1400) (ASTM D638)
  • Vicat Softening Point in °C(°F) 95°C (203°F)

此材料没有安全数据说明书
如需了解更多信息,请 联系陶氏

没有找到此材料按所选语言显示的销售规格

DOW™ 955I Low Density Polyethylene Resin
该产品暂无技术数据表
如需了解更多信息,请 联系陶氏

DOW™ 955I Low Density Polyethylene Resin


该产品暂无法规信息说明书


DOW™ 955I Low Density Polyethylene Resin
如需了解该产品的经销商选项,请 联系陶氏