2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
655 (95000) - Method 1 (3 point load)
|
Bottles and Drums Use
|
Food, Household Industrial Chemicals (HIC) / Agriculture Bottles
|
Brittleness Temperature in °C(°F)
|
-76.1 (<-105) - Plaque Molded, <-95.0 (<-139) - Compression Molded
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
>2000hr - F0 - Compression Molded
|
Fabrication Method
|
Blown Film Extrusion, Compression Molding, Pipe Extrusion
|
Functionality
|
Mechanical Performance
|
Impact Strength in MPa (psi)
|
231 (110) - Type S
|
Tensile Elongation at Break, MD
|
>800 - Compression Molded %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
20.7 (3000) - Compression Molded
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
19.0 (2750) - Compression Molded
|
Vicat Softening Point in °C(°F)
|
120 (248)
|