Brittleness Temperature in °C(°F)
|
-52.8 (-63.0)
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
6.00 hr - 50˚C (122˚F) F50
|
Fabrication Method
|
Injection Molding
|
Functionality
|
Mechanical Performance
|
Impact Strength in MPa (psi)
|
90.4 (43.0)
|
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238))
|
62
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
62
|
Structure Type
|
Monolayer, Multilayer
|
Tensile Elongation at Break, MD
|
37 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
18.6 (2700)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
14.5 (2100)
|