性能

app.properties.Title

Anti-block No
Slip No

product.use.formulating.properties.Title

Type Non-Breathable Cast Film

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 798 (116000) ASTM D882
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 935 (136000) ASTM D882
Brittleness Temperature in °C(°F) < -76.1
Density 0.965 g/cm3
Density Range .961+
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 2 hr
Fabrication Method Cast Film Extrusion, Film Extrusion, Injection Molding
Functionality Mechanical Performance
Impact Strength in MPa (psi) 168 kJ/m2 (80 ft lb/in2) ASTM D1822
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 8.3
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) .579 ()
Structure Type Monolayer, Multilayer
Tensile Elongation at Break, MD 670 %
Tensile Elongation at Break, TD 490 %
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 22.4 (3240) ASTM D882
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 20.4 (2950) ASTM D882