性能

app.properties.Title

Anti-block No
Collation Shrink Usage Logistics, Retail
Slip No
Tie Layers No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 200 (29000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 228 (33000)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 170 g
Density 0.919 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 220 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 210 g
Fabrication Method Blown Film Extrusion, Blown Film Extrusion
Functionality Processing
Gloss (45 degree) 34
Haze (ASTM D1003) 18 %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.22
Melting Point, DSC (Dow Method) in °C(°F) 109 (228)
Tensile Elongation at Break, MD 220 %
Tensile Elongation at Break, TD 500 %
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 11 (1600)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11 (1600)